1. Material: Natural high grade rubber latex, in compliance with ISO 2004.
2. Particle Count: Max. 2000 /cm2 (Tested in accordance to IES-RP-CC-005.2)
3. Protein Level: Below 50 μg/g. (Tested in accordance to ASTM D5712-95)
4. Trace Elements: Trace elements (symbol) Maximum
Fluoride (F) 1.0 μg/cm2
Chloride (Cl) 2.5 μg/cm2
Bromide (Br) 1.0 μg/cm2
Nitrate (NO3) 1.0 μg/cm2
Phosphate (PO4) 1.0 μg/cm2
Sulfate (SO4) 1.0 μg/cm2
Sodium (Na) 1.0 μg/cm2
Potassium ( K) 1.0 μg/cm2
(Tested in accordance to IES-RP-CC-005.2)

5. Copper Strip Test: No discolouration.
6. FTIR: Silicone oil, Amide, DOP not detectable. (Tested in accordance to IES-RP-CC-005.2)
7. Non-volatile residue: Max. 30 mg/g. (Tested in accordance to IES-RP-CC-005.2)
8. Color: Off white to yellow.
9. Design and Feature: Ambidextrous, textured or smooth and beaded cuff.
10. Dimensions: Glove size Palm width (mm) Length (mm)
Extra-small 70±10 min. 240mm
Small 80±10 min. 240mm
Medium 95±10 min. 240mm
Large 110±10 min. 240mm
Extra-large 115±10 min. 240mm

11. Thickness: Location of thickness measurements Double wall (mm)
Finger (at 15mm from fingertip) min. 0.28mm
Palm (at center of palm) min. 0.20mm
12. Physical Properties: Before aging After aging
Tensile Strength (Mpa): Min. 21 (Before aging) min. 16 (After aging)
Ultimate Elongation (%): Min. 700 (Before aging) min. 500 (After aging)
13. Packaging: 100 pieces of gloves per double polybags, 10 polybags per master polybag, 1 master polybag per carton.
Note: Inner & outer polybags are manufactured & processed in Class 100 Cleanroom

14. Certificate of Conformance: A certificate of conformance is available upon request to ensure all products shipped conform to specified specifications.
15. Quality Assurance: Manufactured under ISO 9002 Quality System.
Meet or exceed ASTM D3578-95 on water leak & dimension.
The information above is a guideline of typical performance values and characteristics of the products & not to be use as actual product specifications.

Standard:SGS